About ASTM A302
This specification covers manganese-molybdenum and manganese-molybdenum-nickel alloy steel plates intended particularly for welded boilers and other pressure vessels. ASTM A302 is a kind of low alloy steel specification covers 4 different grades(A, B, C, D), Grade C and D contains chemical composition Ni, with the same thickness, yield and tensile strength of Grade C is the same of Grade B, while elongation rate of grade C is higher.This specification covers manganese-molybdenum and manganese-molybdenum-nickel alloy steel plates intended particularly for welded boilers and other pressure vessels. ASTM A302 is a kind of low alloy steel specification covers 4 different grades(A, B, C, D), Grade C and D contains chemical composition Ni, with the same thickness, yield and tensile strength of Grade C is the same of Grade B, while elongation rate of grade C is higher. It is manufactured for Pressure Vessel, Boiler, Storage Tanks and Heat Exchanger in Oil, Gas Project.
We can offer ASTM A302/A302M A302 Grade B,A302 Gr.B Boiler and Pressure vessel steel
Pressure vessel steel plate ASTM A302/A302M A302 Grade B under steel standard ASME SA302/SA302M which is manganese-molybdenum alloy steel plates intended particularly for welded boilers and other pressure vessels.
According to their strength levels,there are different grades A302 Grade A,A302 Grade B,A302 Grade C and A302 Grade D.Pressure vessel steel plate A302 Grade A owned tensile strength within 515-655 Mpa,minimum yield strength is 310 Mpa,and pressure vessel steel plate A302 Grade B owned tensile strength at 550-690 Mpa.
Steel Standard: ASTM A302/A302M
Thickness:6mm-450mm
Width:1200mm-4200mm
Length:3000mm-18000mm
Surface Treatment:Shot blasting and painting or coated
Mechanical Property
|
Steel Grade |
|
ASTM A302 Mechanical Property |
||
|
Thickness |
Yield |
Tensile |
Elongation |
|
|
A302 Grade A |
mm |
Min Mpa |
Mpa |
Min % |
|
6-50 |
310 |
515-655 |
19% |
|
|
50-200 |
310 |
515-655 |
15% |
|
|
A302 Grade B |
6-50 |
345 Mpa |
550-690 Mpa |
18% |
|
50-200 |
345 Mpa |
550-690 Mpa |
15% |
|
|
A302 Grade C |
6-50 |
50 [345] |
80-100kis [550-690]Mpa |
17% |
|
50-200 |
20% |
|||
|
Composition |
Type |
Thickness (mm) |
A |
B |
C |
D |
|
C ≤ |
Heat analyse |
≤25 |
0.20 |
0.20 |
0.20 |
0.20 |
|
Product analyse |
50~100 |
0.23 |
0.23 |
0.23 |
0.23 |
|
|
＞100 |
0.25 |
0.25 |
0.25 |
0.25 |
||
|
Mn ≤ |
Heat analyse |
- |
0.95~0.13 |
1.15~1.50 |
1.15~1.50 |
1.15~1.50 |
|
Product analyse |
- |
0.87~1.41 |
1.07~1.62 |
1.07~1.62 |
1.07~1.62 |
|
|
P ≤ |
Heat analyse |
- |
0.035 |
0.035 |
0.035 |
0.035 |
|
S ≤ |
Product analyse |
- |
0.040 |
0.035 |
0.035 |
0.035 |
|
Si |
Heat analyse |
- |
0.15~0.40 |
0.15~0.40 |
0.15~0.40 |
0.15~0.40 |
|
Product analyse |
- |
0.13~0.45 |
0.13~0.45 |
0.13~0.45 |
0.13~0.45 |
|
|
Mo |
Heat analyse |
- |
0.45~0.60 |
0.45~0.60 |
0.45~0.60 |
0.45~0.60 |
|
Product analyse |
- |
0.41~0.64 |
0.41~0.64 |
0.41~0.64 |
0.41~0.64 |
|
|
Ni |
Heat analyse |
- |
- |
- |
0.40~0.70 |
0.70~1.00 |
|
Product analyse |
- |
- |
- |
0.37~0.73 |
0.67~1.03 |
|
Grade |
Strength Level (N/mm2) |
|
|
Yield Strength [MPa] |
Tensile Strength [MPa] |
|
|
A302GrA |
315 |
520 |
|
A302GrB |
345 |
550 |
|
A302GrC |
345 |
550 |
|
A302GrD |
345 |
550 |