Steel Grade

carbon steel plate,steel coil,stainless steel plate,china export service provider.

Centerway Steel Co., Ltd,stainless steel plate&sheet,coils manufacturers&factory

Back |You are in : Home > News > Steel Grade

Product Gategory

Send Email To Us

Services

GB/T16270 Steel Plate

Date:2022-05-06View:803Tags:

GB/T16270 Q500E

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	1.7	0.025	0.015	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	17			J	J	J	J
500	480	440	590-770	590-770	540-720	17			47	47	34	34

GB/T16270 Q550C

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	1.7	0.025	0.015	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	16			J	J	J	J
550	530	490	640-820	640-820	590-770	16			47	47	34	34

GB/T16270 Q550D

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	1.7	0.02	0.010	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	16			J	J	J	J
550	530	490	640-820	640-820	590-770	16			47	47	34	34

GB/T16270 Q550E

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	1.7	0.025	0.015	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	16			J	J	J	J
550	530	490	640-820	640-820	590-770	16			47	47	34	34

GB/T16270 Q550F

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	1.7	0.02	0.010	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	16			J	J	J	J
550	530	490	640-820	640-820	590-770	16			47	47	34	34

GB/T16270 Q620C

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	1.7	0.025	0.015	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	15			J	J	J	J
620	580	560	700-890	700-890	650-830	15			47	47	34	34

GB/T16270 Q620D

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	1.7	0.02	0.010	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	15			J	J	J	J
620	580	560	700-890	700-890	650-830	15			47	47	34	34

GB/T16270 Q620E

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	1.7	0.025	0.015	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	15			J	J	J	J
620	580	560	700-890	700-890	650-830	15			47	47	34	34

GB/T16270 Q620F

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	1.7	0.02	0.010	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	15			J	J	J	J
620	580	560	700-890	700-890	650-830	15			47	47	34	34

GB/T16270 Q690C

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	1.8	0.025	0.015	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	14			J	J	J	J
690	650	630	770-940	760-930	710-900	14			47	47	34	34

GB/T16270 Q690D

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	1.8	0.02	0.010	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	14			J	J	J	J
690	650	630	770-940	760-930	-	14			47	47	34	34

GB/T16270 Q690E

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	1.8	0.025	0.015	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	14			J	J	J	J
690	650	630	770-940	760-930	-	14			47	47	34	34

GB/T16270 Q690F

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	1.8	0.02	0.01	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	14			J	J	J	J
690	650	630	770-940	760-930	-	14			47	47	34	34

GB/T16270 Q800C

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	2.0	0.025	0.015	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	13			J	J	J	J
800	740	-	840-1000	800-1000	-	13			34	34	27	27

GB/T16270 Q800D

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	2.0	0.02	0.010	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	13			J	J	J	J
800	740	-	840-1000	800-1000	-	13			34	34	27	27

GB/T16270 Q800E

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	2.0	0.025	0.015	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	13			J	J	J	J
800	740	-	840-1000	800-1000	-	13			34	34	27	27

GB/T16270 Q800F

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	2.0	0.02	0.010	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	13			J	J	J	J
800	740	-	840-1000	800-1000	-	13			34	34	27	27

GB/T16270 Q890C

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	2.0	0.025	0.015	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	11			J	J	J	J
890	830	-	940-1100	800-1100	-	11			34	34	27	27

GB/T16270 Q890D

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	2.0	0.02	0.010	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	11			J	J	J	J
890	830	-	940-1100	-	-	11			34	34	27	27

GB/T16270 Q890E

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	2.0	0.025	0.015	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	11			J	J	J	J
890	830	-	940-1100	-	-	11			34	34	27	27

GB/T16270 Q890F

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	2.0	0.02	0.010	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	11			J	J	J	J
890	830	-	940-1100	-	-	11			34	34	27	27

GB/T16270 Q960C

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	2.0	0.025	0.015	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	10			J	J	J	J
960	-	-	980-1150	-	-	10			34	34	27	27

GB/T16270 Q960D

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	2.0	0.02	0.010	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	10			J	J	J	J
960	-	-	980-1150	-	-	10			34	34	27	27

GB/T16270 Q960E

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	2.0	0.025	0.015	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	10			J	J	J	J
960	-	-	980-1150	-	-	10			34	34	27	27

GB/T16270 Q960F

C% max	Si% max	Mn% max	P% max	S% max	Cu% max	Cr% max	Ni% max	Mo % max	B % max	V % max	Nb% max	Ti % max
0.2	0.80	2.0	0.02	0.010	0.5	1.5	2	0.70	0.005	0.12	0.06	0.05
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			Energy and temperature
Re yield strength Mpa min			Re yield strength Mpa min			elongation% min			0	-20	-40	-60
t≤50	50-100	100-150	t≤50	50-100	100-150	10			J	J	J	J
960	-	-	980-1150	-	-	10			34	34	27	27

【Prev】 : GB/T1591 Steel Plate
【Next】 : The thickness tolerance of stainless steel plate

You are welcome to leave us a message

Product Category

Copper Material

Nickel Alloy Product

Duplex Stainless Steel

Stainless Steel Plate

Stainless Steel Profile Steel

Stainless Steel Coil

Steel Plate

Service

Quality Assurance

Packing

Warehouse

Customized service

Contact info

NO.246 Shidai Yangguang Blvd, Yuhua District, Changsha, Hunan, China.
0086-731-86452683，86452691，86452692，86452693
sales@ctwsteel.com

We use cookies and other tracking technologies to improve your browsing experience on our website, to show you personalized content and targeted ads, to analyze our website traffic, and to understand where our visitors are coming from,This behavior is in compliance with the user consent policy.

Decline

Steel Grade

Steel Grade

Quality Assurance

Packing

Warehouse

Customized service

GB/T16270 Steel Plate

Recommended Products

You are welcome to leave us a message

Product Category

Service

Contact info